Liquid filtration using an anionic microporous membrane

ABSTRACT

A novel hydrophilic anionic charge modified microporous filter membrane is provided comprising an organic polymeric microporous filter membrane having a micro-structure throughout the membrane and a modifying amount of an anionic charge modifying agent bound to substantially all of the membrane micro-structure without substantial pore size reduction or pore blockage. 
     The invention is further directed to a process for anionically charge modifying an organic polymeric microporous filter membrane by applying to the membrane the charge modifying agent, preferably, by contacting the membrane with a solution of the charge modifying agent. 
     The anionic modified microporous membrane of this invention may be used for the filtration of fluids, particularly parenteral or biological liquids contaminated with charged particulates, and for plasmapheresis, particularly in the form of hollow fiber tubes. The membrane has low extractables and is sanitizable or sterilizable.

BACKGROUND OF THE INVENTION

1. Field Invention

This invention relates to microporous membranes, and more particularly to anionic charge modified microporous membranes suitable for the filtration of aqueous fluids, such as biological liquids and for plasmapheresis.

2. Prior Art

Microporous membranes are well known in the art. For example, U.S. Pat. No. 3,876,738 to Marinaccio et al (1975) describes a process for preparing a microporous membrane, for example, by quenching a solution of a film forming polymer in a nonsolvent system for the polymer. European Patent Application No. 0 005 536 (1979) and U.S. Pat. No. 4,340,479 both to Pall describe a similar process.

Other processes for producing microporous membranes are described, for example, in the following U.S. Patents:

U.S. Pat. No. 3,642,668 to Bailey et al (1972);

U.S. Pat. No. 4,203,847 to Grandine,II (1980);

U.S. Pat. No. 4,203,848 to Grandine,II (1980); and

U.S. Pat. No. 4,247,498 to Castro (1981).

Commercially available microporous membranes, for example, made of nylon, are available from Pall Corporation, Glen Cove, N.Y. under the trademark ULTIPOR N₆₆. Another commercially significant membrane made of polyvinylidene fluoride is available from Millipore Corp., Bedford, Mass. under the trademark DURAPORE. This membrane is probably produced by the aforementioned Grandine,II patents. Such membranes are advertised as useful for the sterile filtration of pharmaceuticals, e.g. removal of microorganisms.

Various studies in recent years, in particular Wallhausser, Journal of Parenteral Drug Association, June 1979, Vol. 33 #3, pp. 156-170, and Howard et al, Journal of the Parenteral Drug Association, March-April, 1980, Volume 34, #2 pp. 94-102, have reported the phenomena of bacterial break-through in filtration media, in spite of the fact that the media had a low micrometer rating. For example, commercially available membrane filters for bacterial removal are typically rated as having an effective micrometer rating for the microreticulate membranes structure of 0.2 micrometers or less, yet such membranes typically have only a 0.357 effective micrometer rating for spherical contaminant particles, even when rated as absolute for Ps. diminuta, the conventional test for bacterial retention. Thus passage of few microorganisms through the membrane may be expected under certain conditions and within certain limits. This problem has been rendered more severe as the medical uses of filter membranes increases. Brown et al highlights this problem in CRC Critical Reviews in Environment Control, March 1980, page 279 wherein increased patient mortality and morbidity derived from contamination of sterile solutions for topical, oral, and intravenous therapy are reported.

One method of resolving this problem and its inevitable consequences, is to prepare a tighter filter, i.e. one with a sufficiently small effective pore dimension to enable the capture of the fine particulate, e.g., microorganisms, by mechanical sieving. Such filter structures, in the form of microporous membranes of 0.1 micrometer rating or less, may be readily prepared. The flow rate, however, exhibited by such structures at conventional pressure drops is low. Thus such modification of the internal geometry, i.e. pore size, of the microporous membrane is not an economical solution to the problem of bacterial breakthrough.

Attempts to increase the short life of filter media due to pore blockage and enhance flow rates through filter media having small pores have been made by charge modifying the media by various means to enhance capture potential of the filter. For example, U.S. Pat. Nos. 4,007,113 and 4,007,114 to Ostreicher, describes the use of a melamine formaldehyde cationic colloid to charge modify fibrous and particulate filter elements; U.S. Pat. No. 4,305,782, to Ostreicher et al describes the use of an inorganic cationic colloidal silica to charge modify such elements; and U.S. Ser. No. 164,797 filed June 30, 1980, to Ostreicher et al, describes the use of a polyamido-polyamine epichlorhydrin cationic resin to charge modify such filter elements. Similar attempts at cationic charging of filter elements were made in U.S. Pat. Nos. 3,242,073 (1966) and 3,352,424 (1967) to Guebert et al; and U.S. Pat. No. 4,178,438 to Hasse et al (1979).

Cationically charged membranes which are used for the filtration of anionic particulate contaminants are also known in the art. For Example charge modified filter membranes are disclosed in the Assignee's Japanese Pat. No. 923649 and French Pat. No. 7415733. As disclosed therein, an isotropic cellulose mixed ester membrane, was treated with a cationic colloidal melamine formaldehyde resin to provide charge functionality. The membrane achieved only marginal charge modification. Additionally, the membrane was discolored and embrittled by the treatment, extractables exceeded desirable limits for certain critical applications, and the membrane was not thermally sanitizable or sterilizable. Treatment of the nylon membranes prepared by the methods described in U.S. Pat. No. 2,783,894 to Lovell (1957) and U.S. Pat. No. 3,408,315 to Paine (1968) is suggested. Nylon membranes so treated also demonstrate marginal charge modification, high extractables and/or are not thermally sanitizable or sterilizable.

Assignee in order to solve the aforementioned problems has developed unique cationic charge modified microporous membranes for use in the filtration of fluids. These cationic membranes, their preparation and use are described and claimed in U.S. patent application Ser. No. 268,543, filed on May 29, 1981 in the name of Barnes et al, now U.S. Pat. No. 4,473,475 and EPC Pub. Nos. 0066 814, and U.S. patent application Ser. No. 314,307, filed on Oct. 23, 1981 in the name of Ostreicher et al, now U.S. Pat. No. 4,473,475 and EPC Pub. Nos. 0050 864.

Cationic charge modified nylon membranes covered by these inventions are now being sold by AMF CUNO Division under the trademark ZETAPOR. Pall Corp., Glen Cove, N.Y. is also selling a cationic charge modified nylon membrane under trademark N₆₆ POSIDYNE.

To Applicant's knowledge, prior to this invention, no one has produced a useful anionically charged microporous filter membrane for the removal of fine charged particulates from liquids nor has anyone used charge modified microporous filter membrane for cross-flow filtration.

There are numerous references which describe the treatment of reverse osmosis, ultrafiltration, semipermeable type membranes for various objects. See for example, U.S. Pat. Nos. 3,556,305 to Shorr (1971), 3,556,992 to Massuco (1971), 3,944,485 (1976) and 4,045,352 (1977) to Rembaum et al, 4,005,012 to Wrasidlo (1977), 4,125,462 to Latty (1978), 4,214,020 to Ward et al (1980), and 4,239,714 to Sparks et al (1980). Membranes have also been treated to produce anionic ultrafiltration, reverse osmosis, semipermeable type membranes. For example, see the following U.S. Patents:

U.S. Pat. No. 3,004,904 to Gregor (1961) describes an electronegative selective permeable membrane cast from a mixture of a film forming polymer and a substantially linear electronegative polyelectrolyte. Preferably, the membrane is a mixture of a polyvinyl-type resin and a water soluble substantially linear polyvinyl-type polyelectrolyte film. The film is produced by casting an organic solvent solution of the polymer and polyelectrolyte. A number of polyelectrolytes are listed including polyacrylic acid and "carboxylic acid groups".

U.S. Pat. No. 3,524,546 to Hoehn et al, (1970) describes permeation membranes of graft copolymers of nylon produced by grafting at least 300 titratable acid groups on to the polymer chain per million grams of polymer. A preferred material for grafting onto the polymer is polymerizable organic acid, e.g. acrylic acid. A sufficient amount of grafting is said to be when the graft copolymer shows a grafted weight gain of acrylic acid of about 3%. The only methods described for performing such grafting are by high energy ionizing radiation or by the action of free radical generating catalysts. In Example 1, a nylon film was grafted by swelling the film with acrylic acid and then subjecting the film to radiation under an electron beam. The grafted membranes are said to be physically strong, having exceptionally advantageous throughput rates when compared to known permeation membranes.

U.S. Pat. No. 3,672,975 to Arons (1972) describes the copolymerization of polyacrylic acid within a nylon structure. The copolymer is said to have excellent enhanced properties suitable for textile applications, e.g. high moisture sorption, and high melting point. Prior to Arons, in order to form such nylon structures acrylic acid monomer was diffused into the nylon structure and caused to homopolymerize and to graft to the nylon simultaneously. It was also known, prior to Arons, to chemically combine a surface finish of completely polymerized polyacrylic acid to nylon by means of heat curing. Arons improves on these known processes by using a preformed polymer of acrylic acid and copolymerizing it within the nylon structure. The process is accomplished by diffusing the preformed polyacrylic acid under certain prescribed conditions, e.g. pH of 1.5 to 3.5, 1 to 5 hours and 80° to 150° C. Arons indicates that the polyacrylic acid appears to attach to the terminal amine groups of the nylon.

U.S. Pat. No. 3,752,749 to Gregor, (1973) describes the use of cation- and anion-exchange membranes for the electrodialytic concentration and removal of acids from aqeuous effluents. The cation exchange membrane is described as " . . . a homogeneous sheet of insoluble ionexchange material containing sulfonic acid groups or supporting matrix impregnated with a similar material."

U.S. Pat. Nos. 3,808,305 (1974) and 4,012,324 (1977) to Gregor describes a fixed charged (negative or positive) membrane prepared by casting a solution which includes a matrix polymer, a polyelectrolyte and a cross-linking agent to form a film. The membrane is useful for ion exchange membranes, electrodialysis, ultrafiltration, etc. Suitable matrix polymers include nylon 6 and nylon 66. The only polyelectrolytes listed are sulfonic acid polyelectrolytes such as polystyrene sulfonic acid, the sodium salt of polystyrene sulfonic acid, sulfonated polymethyl styrene, and copolymers thereof with other vinyl monomers, polyvinyl sulfonic acid, sulfonated polyvinyl naphthalenes, sulfonated polyvinyl anthracenes, sulfonated linear phenol formaldehyde resins, condensation polyamides and polyesters containing comonomers such as sulfoisophthalic acid salts.

U.S. Pat. No. 4,033,817 to Gregor (1977) describes pressure-driven enzyme coupled membranes composed of a polymeric matrix cast from an interpolymer mixture which includes " . . . polystyrenesulfonic acid (to) provide for a higher polar negative charge within the membrane, and can be used together with a coupling agent such as polyacrylic acid." The homopolymers and copolymers of maleic anhydride may also be included in the interpolymer mixture.

U.S. Pat. No. 4,214,020 to Ward et al (1980) is directed to coating the exteriors of hollow fiber semipermeable membranes. The coatings provide the desired selective separation and/or desirable flux. The process described in Ward et al involves immersing a bundle of hollow fibers in a coating liquid containing materials suitable for forming the coating and providing a sufficient pressure drop from the exterior of the hollow fiber. Material suitable for forming the coating should have a sufficiently large molecular size or particle size so that the material does not readily pass through the pores in the walls of the hollow fibers when subjected to the pressure drop used in the process. The pores in the hollow fibers are said to have an average cross-sectional diameter less than about 20,000 angstroms, and preferably less than about 1000 to 5000 angstroms. Nylon is a material of choice for the hollow fibers. The depositable material may be a poly(alkyl acrylates) and poly(alkyl methacrylates) wherein the alkyl groups have, say 1 to about 8 carbons.

U.S. Pat. No. 4,250,029 to Kiser et al (1981) is directed to coated membranes having two or more coatings of polyelectrolytes with oppositely charged adjacent pairs separated by a layer of material which substantially prevents charge neutralization. The membranes coated are ultrafiltration, reverse osmosis and electrodialysis filtration membranes. Preferred membranes are said to be aliphatic and aromatic nylons. The anionics useful are said to be polymeric anionic polyelectrolytes of relatively high molecular weight, i.e. above 50,000 preferably above 500,000. Kiser et al states that since the anionics are preferably applied as a final coating, after the cationic and on the same side of the membrane as the coatings, there is no essential requirement that the anionic be substantive to the membrane, i.e., the opposite charge of the previously applied cationic coating is sufficient to bind the anionic polyelectrolyte. However, when both the cationic and anionic polyelectrolyte coatings are to be applied to the same side of a membrane they may be separated by a nonionic or neutral layer which may be deposited in the same manner as the polyelectrolytes. This neutral layer separates the oppositely charged polyelectrolyte coating preventing neutralization of the charges. Among specific polyelectrolytes having an anionic charge is poly(acrylic) acid. It is stated, however, that when a coating of cationic material is followed by an anionic layer with little or no neutral layer between the charged layers, the permeation properties of a hollow fiber membrane seems to decrease, as compared to a single layer coating.

OBJECTS AND SUMMARY OF THE INVENTION

It is an object of this invention to provide a novel anionic charge modified microporous filter membrane, particularly suitable for the filtration of biological or parenteral liquids.

It is a further object of this invention to provide a process for anionically charge modifying an organic polymeric microporous filter membrane.

It is still a further object of this invention to provide a process for the filtration of fluids, in particular the filtration of biological or parenteral liquids.

It is another object of this invention to provide an isotropic anionic charge modified microporous filter membrane which has low extractables suitable for the filtration of biological or parenteral liquids or for plasmapheresis.

It is yet another object of this invention to prepare a sanitizable or sterilizable anionically charge modified microporous membrane for the efficient removal of charged particulate contaminants from contaminated liquids, particularly without the adsorption of desirable anionic constituents contained therein.

It is a further object of this invention to enhance the filtration performance of a preformed microporous membrane for charged particulate contaminants without decreasing the pore size of the membrane.

It is still a further object of this invention to provide a microporous membrane capable of capturing charged particulate contaminant of a size smaller than the effective pore size of the membrane.

These and other objects of this invention are attained by a novel hydrophilic anionic charge modified microporous filter membrane. The membrane comprises a hydrophilic organic polymeric microporous membrane having a microstructure throughout the membrane and a charge modifying amount of an anionic charge modifying agent bonded to substantially all of the membrane microstructure without substantial pore size reduction or pore blockage.

The invention is further directed to a process for anionically charge modifying a hydrophilic organic polymeric microporous membrane by applying to the membrane the charge modifying agent. Preferably, the process for charge modifying the microporous membrane comprises contacting the membrane with an aqueous solution of the charge modifying agent.

The preferred microporous filter membrane is nylon. The preferred anionic charge modifying agents have carboxyl (COOH) or sulfonic (SO₃ H) anionic functional substituents.

The anionic charge modified microporous membrane of this invention may be used for the filtration of fluids, particularly parenteral or biological liquids and for cross-flow filtration, e.g. plasmapheresis. The membrane may, for example, be in the form of films or hollow tubes.

BRIEF DESCRIPTION OF THE FIGURES

FIG. 1 is a schematic of the system employed in Example IV herein.

FIG. 2 is a summary plot of the five membranes evaluated in Example IV.

FIG. 3 is a schematic of the system employed in Example V herein.

FIGS. 4-7 are summary plots for Example V herein.

DETAILED DESCRIPTION OF THE INVENTION

The anionic charge modified microporous membrane of this invention is produced from organic polymeric microporous membrane. Such membranes are well known in the art.

By the use of the term "microporous filter membrane" as used herein, it is meant an asymmetric or symmetric, microporous membrane having a pore size of at least 0.05 microns or larger, or an initial bubble point (IBP), as that term is used herein, in water of less than 120 psi. A maximum pore size useful for this invention is about 1.2 micron or an IBP of greater than about 10 psi. Additionally, the membrane has a fine microstructure throughout the membrane. By "symmetrical" it is meant that the pore structure is substantially the same on both sides and throughout the membrane. By the use of the term "asymmetric" it is meant that the pore size differs from one surface to the other. A number of commercially available membranes not encompassed by the term "microporous filter membrane" are those having one side formed with a thin skin which is supported by a much more porous open structure which are typically used for reverse osmosis, ultrafiltration and dialysis. Thus by the use of the term "microporous filter membrane" it is meant membranes suitable for the removal of suspended solids and particulates from fluids which permit dissolved solids to pass therethrough. These membranes, however, may have other uses both known and unknown.

By the use of the term "hydrophilic" in describing the preformed and the anionic microporous membrane of this invention, it is meant a membrane which adsorbs or absorbs water. Generally, such hydrophilicity is produced by a sufficient amount of hydroxyl (OH--), carboxyl (--COOH), amino (--NH₂) and/or similar functional groups on the surface of the membrane. Such groups assist in the adsorption and/or absorption of water onto the membrane. Such hydrophilicity of the membrane and internal microstructure (which may be obtained or enhanced by treatment of the preformed membrane) is a necessary element for the preformed membrane which is treated in order to provide the adequate inclusion of the anionic charge modifying agent to the microporous membrane internal microstructure. Such hydrophilicity of the anionic membrane of this invention is necessary in order to render the membrane more useful for the filtration of aqueous fluids.

A preferred microporous filter membrane is one produced from nylon. The term "nylon" is intended to embrace film forming polyamide resins including copolymers and terpolymers which include the recurring amido grouping. While, generally, the various nylon or polyamide resins are all copolymers of a diamine and a dicarboxylic acid, or homopolymers of a lactam or an amino acid, they very widely in crystallinity or solid structure, melting point, and other physical properties. Preferred nylons for use in this invention are copolymers of hexamethylene diamine and adipic acid and homopolymers of poly-o-caprolactam.

Alternatively, these preferred polyamide resins have a ratio of methylene (CH₂) to amide (NHCO) groups within the range about 5:1 to about 8:1, most preferably about 5:1 to about 7:1. The preferred nylon 6 and nylon 66 each have a ratio of 6:1, whereas nylon 610 has a ratio of 8:1.

The nylon polymers are available in a wide variety of grades, which vary appreciably with respect to molecular weight, within the range from about 15,000 to about 42,000 and in other characteristics.

The highly preferred species of the units comprising the polymer chain is polyhexamethylene adipamide, i.e. nylon 66, and molecular weights in the range above about 30,000 are preferred. Polymers free of additives are generally preferred, but the addition of antioxidants or similar additives may have benefit under some conditions.

The preferred membrane substrates are produced by the method disclosed in U.S. Pat. No. 3,876,738 to Marinaccio et al. Another similar method of producing such membranes is described in European Patent Application No. 0 005 536 and U.S. Pat. No. 4,340,479 to Pall. The entire disclosures of all of these references are incorporated herein by reference.

Additionally, any of the hydrophilic microporous membranes commercially available, for example, Pall Corp.'s ULTIPOR N₆₆ (nylon), Millipore's DURAPORE (polyvinylidene fluoride) and cellulose acetate/nitrate membranes, produced by numerous companies, having characteristics potentially suitable for fine filtration of fluids, particularly aqueous systems, are suitable for treatment in accordance with this invention.

The preferred Marinaccio et al process for producing membrane develops a unique fine microstructure throughout the membrane through the quench technique described therein, offering a superior substrate for filtration. Broadly, Marinaccio et al produces microporous films by casting or extruding a solution of a film-forming polymer in a solvent system into a quenching bath comprised of a non-solvent system for the polymer. Although the non-solvent system may comprise only a non-solvent, the solvent system may consist of any combination of materials provided the resultant non-solvent system is capable of setting a film and is not deleterious to the formed film. For example, the non-solvent system may consist of materials such as water/salt, alcohol/salt or other solvent-chemical mixtures. The Marinaccio et al process is especially effective for producing nylon films. More specifically, the general steps of the process involve first forming a solution of the film-forming polymer, casting the solution to form a film and quenching the film in a bath which included a non-solvent for the polymer.

The nylon solutions which can be used in the Marinaccio et al process include solutions of certain nylons in various solvents, such as lower alkanols, e.g., methanol, ethanol and butanol, including mixtures thereof. It is known that other nylons will dissolve in solutions of acids in which it behaves as a polyelectrolyte and such solutions are useful. Representative acids include, for example, formic acid, citric acid, acetic acid, maleic acid and similar acids which react with nylons through protonation of nitrogen in the amide group characteristic of nylon.

The nylon solutions are diluted with non-solvent for nylon, the non-solvent employed being miscible with the nylon solution. Dilution with non-solvent may, according to Marinaccio et al, be effected up to the point of incipient precipitation of the nylon. The non-solvents are selected on the basis of the nylon solvent utilized. For example, when water-miscible nylon solvents are employed, water can be employed. Generally, the non-solvents can be methyl formate, aqueous lower alcohols, such as methanol and ethanol, polyols such as glycerol, gycols, polyglycols, and ethers and esters thereof, water and mixtures of such compounds. Moreover, salts can also be used to control solution properties.

The quenching bath may or may not be comprised of the same non-solvent selected for preparation of the nylon solution and may also contain small amounts of the solvent employed in the nylon solution. However, the ratio of solvent to non-solvent is lower in the quenching bath than in the polymer solution in order that the desired result be obtained. The quenching bath may also include other non-solvents, e.g., water.

The formation of the polymer film or hollow tubes can be accomplished by any of the recognized methods familiar to the art. The preferred method of forming the film is casting using a knife edge which controls the thickness of the cast film. The thickness of the film will be dictated by the intended use of the microporous product. In general, the films will be cast at thickness as in the range of from about 1 mil. to about 20 mils., preferably from about 1 to about 10 mils. Preferably, the polymer solution is cast and simultaneously quenched, although it may be desirable to pass the cast film through a short air evaporation zone prior to the quench bath. This latter technique is, however, not preferred. After the polymer solution is cast and quenched, it is removed from the quench bath and preferably washed free of solvent and or non-solvent. Subsequently the film can be at least partially dried and then treated in accordance with this invention. Hollow tubes are formed by extrusion over a fluid core and quenching in an appropriate bath using appropriately designed and shaped nozzles. Such methods are well known in the art.

Pall's aforementioned European Patent Application No. 0 005 536 and U.S. Pat. No. 4,340,479 describe a similar method for the conversion of polymer into microporous membrane which may be used. Broadly, Pall provides a process for preparing skinless hydrophilic alcohol-insoluble polyamide membranes by preparing a solution of an alcohol-insoluble polyamide resin in a polyamide solvent. Nucleation of the solution is induced by the controlled addition to the solution of a non-solvent for the polyamide resin, under controlled conditions of concentration, temperature, addition rate, and degree of agitation to obtain a visible precipitate of polyamide resin particles (which may or may not partially or completely redissolve) thereby forming a casting solution.

The casting solution is then spread on a substrate to form a thin film. The film is then contacted and diluted with a mixture of solvent and non-solvent liquids containing a substantial proportion of the solvent liquid, but less than the proportion in the casting solution, thereby precipitating polyamide resin from the casting solution in the form of a thin skinless hydrophilic membrane. The resulting membrane is then washed and dried.

In Pall's preferred embodiment of the process, the solvent for the polyamide resin solution is formic acid and the non-solvent is water. The polyamide resin solution film is contacted with the non-solvent by immersing the film, carried on the substrate, in a bath of non-solvent comprising of water containing a substantial proportion of formic acid.

These preferred nylon membranes, i.e. described in Marinaccio et al and Pall, are characterized by a hydrophilic, isotropic structure, having a high effective surface area and a fine internal microstructure of controlled pore dimensions with narrow pore size distribution and adequate pore volume throughout the membrane structure. For example, a representative 0.22 micrometer rated nylon 66 membrane (polyhexamethylene adipamide) exhibits an initial bubble point (IBP) of about 45 to 50 psid., a foam all over point (FAOP) of about 50 to 55 psid., provides a flow of from 70 to 80 ml/min of water at 5 psid (47 mm. diameter discs), has a surface area (BET, nitrogen adsorption) of about 13 m² /g and a thickness of about 4.5 to 4.75 mils.

The charge modifying agent, e.g., anionic charge modifying agent, is bound to substantially all of the internal microstructure of the microporous membrane. By the use of the term "bound" it is meant that the charge modifying agent is sufficiently attached to or incorporated into the membrane so that it will not significantly extract under the intended conditions of use. By the use of the term "substantially all of the internal microstructure" as used herein it is meant substantially all of the external surface and internal pore surfaces. Typically this is meant the surfaces which are wetted by a fluid, e.g., water, passing through the membrane or in which the membrane is immersed. By the use of the term "charge modifying agent", it is meant a compound or composition that when bound to the microporous filter membrane alters the "zeta potential" of the membrane (see Knight et al, "Measuring the Electrokinetic Properties of Charged Filter Media," Filtration and Separation, pp30-34, Jan./Feb. 1981). The charge modifying agent can be part of the solvent-non-solvent casting system and/or quench bath or a subsequent treatment to the formed membrane.

The anionic charge modifier is a compound or composition which is capable of being bound to the membrane microstructure without substantial pore size reduction or pore blockage and provides a more negative zeta potential to the membrane microstructure. Preferably, such anionic charge modifier is a water soluble compound having substituents capable of binding to the membrane and substituents which are capable of producing a more negative "zeta potential" in the use environment (e.g. aqueous) or anionic functional groups. These functional groups may be carboxyl, phosphonous, phosphonic and sulfonic. Preferably, the charge modifying agent may be a water soluble organic polymer having a molecular weight greater than about 2,000 and less than about 500,000 and capable of of becoming a non-extractable constituent of the membrane.

The charge modifying agent can also be cross-linked to the membrane through a cross-linking agent, for example, an aliphatic polyepoxide having a molecular weight of less than about 500 and, preferably, methylated urea formaldehyde resin and melamine formaldehyde.

The anionic charge modifying agents which may be used in this invention are polymeric anionic polyelectrolytes. Generally, these polyelectrolytes have relatively low molecular weight, e.g. less than 500,000, and are water or other solvent soluble at the desired levels of application. If the anionic agents are applied directly to the membrane it is necessary that they be capable of binding thereto. If they are applied to a cationically charge modified membrane (discussed below), they need only bond to the cationic charge on the membrane. The preferred membrane for use in this invention is nylon produced by process described in the aforementioned Pall and Marinaccio patents, which is inherently charged. This charge may be assist in bonding a charge modifying agent to the membrane.

The anionic charge modifying agent may have either a high or low charge density, or anything between these extremes, however, high charge density is preferred. Specific preferred anionic charge modifying agents useful herein are poly(styrene sulfonic) acid, poly(toluene sulfonic) acid, poly(vinyl sulfonic) acid and poly(acrylic) acid. Other anionic charge modifying agents are poly(methacrylic acid), poly(itaconic acid), hydrolyzed poly(styrene/maleic anhydride) and poly(vinyl phosphonic acid). Additionally, the alkali and alkaline earth metal salts of all of the foregoing may be utilized.

Highly preferred anionic charge modifying agents are poly(styrene sulfonic) acids: ##STR1## having a molecular weight between 2000 and 300,000; and poly(acrylic) acid: ##STR2## having a molecular weight between 2000 and 300,000.

The anionic charge modifying agent may also be cross-linked to the microporous membrane structure through an aliphatic polyepoxide cross-linking agent having a molecular weight of less than about 500. Preferably, the polyepoxide is a di- or tri-epoxide having a molecular weight of from about 146 to about 300. Such polyepoxides have viscosities (undiluted) of less than about 200 centipoise at 25C.

Highly preferred polyepoxides have the formula: ##STR3## wherein R is an alkly of 1 to 6 carbon atoms and n is from 2 to 3. The limitation that the number of carbon atoms in the non-epoxide portion --(R)-- be less than 6 is so that the polyepoxide will be soluble in water or ethanol-water mixtures, e.g. up to 20% ethanol. While higher carbon content materials are functionally suitable, their application would involve the use of polar organic solvents with resulting problems in toxicity, flammability and vapor emissions.

Certain diglycidyl ethers of aliphatic diols may be used as the polyepoxide cross-linking agents. These compounds may be represented as follows: ##STR4##

For example:

When R is (CH₂)₂, HO--R--OH is 1,2-ethanediol

When R is (CH₂)₃, HO--R--OH is 1,3-propanediol

When R is (CH₂)₄, HO--R--OH is 1,4-butanediol

The preferred diglycidyl ether of 1,4-butanediol, is commercially available from Ciba-Geigy, Inc. as RD-2 and from Celanese Corp. as Epi-Rez 5022 and Polyscience.

Other higher carbon diglycidyl ethers may be used as the polyepoxide cross-linking agent, for example when R is (CH₂)₅ the 1,5-pentanediol diglycidyl ether is produced. As stated previously, however, the appropriate polar organic solvents must be used for diluting such polyepoxides.

Triglycidyl ethers, i.e. tri-epoxides may also be utilized as the polyepoxide cross-linking agent. For example, the triglycidyl ether of glycerol may be utilized. These tri-epoxides have the following formula: ##STR5## The triglycidyl ether of glycerol is available from Shell, Inc. as Epon 812 and Celanese Corp. as Epi-Rez 5048.

Another preferred cross-linking agent is methylated urea formaldehyde resin, commercially available from American Cyanamid; for example, Beetle 65, and melamine formaldehyde, e.g., Cymel 303 from American Cyanamide.

Optionally, the anionic charge modifying agent may be applied to a membrane which has been previously treated to produce a hydrophilic cationic charge modified membrane. Preferred membranes and methods of producing such cationic charge modified membranes are described in Assignees aforementioned applications and European publications to Barnes et al (U.S. Ser. No. 268,543 and EPC 066814) and Ostreicher et al (U.S. Ser. No. 314,307 and EPC 0050 864). The entire disclosures of these applications and publications are incorporated herein by reference.

Treating a cationically charge modified membrane in accordance with this invention enhances the bonding of the anionic charge modifier to the membrane and/or reduces the requirements for a cross-linking agent.

An aspect of this invention is directed to the process for anionically charge modifying a hydrophilic organic polymeric microporous membrane, e.g. nylon. The process comprises applying and binding to substantially all of the membrane microstructure, without substantial pore size reduction or pore blockage, a charge modifying amount of the anionic charge modifying agent. Preferably, the process comprises (a) contacting the membrane with an aqueous solution of the anionic charge modifying agent; and (optionally) (b) contacting the membrane with an aqueous solution of the cross-linking agent. The contacting steps may be performed in any order, i.e. step (a) followed by step (b), vice versa or simultaneously. It is preferred, to perform steps (a) and (b) simultaneously to minimize extractables and for ease of manufacture.

In order to provide the charge modifying amount of anionic charge modifying agent to the membrane, it is preferred that the aqueous solution of anionic charge modifying agent that the membrane is contacted with contain at least about 0.5% by weight charge modifying agent in the aqueous solution. The upper range is limited by economic and solubility limitations. For example, an excess of charge modifying agent which is not bonded to the microporous membrane will not be economically utilized and will constitute an undesirable extractive from the membrane. It has been found that the amount of charge modifying agent in the aqueous solution should not exceed about 10% by weight of the solution.

The amount of cross-linking agent used in the aqueous solution is highly dependent on the specific cross-linking agent and the amount and type anionic charge modifying agent used, and the cross-linking mechanism between these compounds to provide the bonding of such charge modifying agent to the microporous membrane. For general guidance however, it has been found that a weight ratio of anionic charge modifying agent to cross-linking agent of from about 1:1 to about 500:1, preferably from about 1:1 to about 20:1 in the aqueous solutions contacted with the membrane, is generally sufficient to provide the binding of the anionic charge modifying agent to the membrane. It has been found that if the aqueous solution containing the cross-linking agent contains at least about 0.1% cross-linking agent by weight of the solution, up to a maximum of about 5% weight of the solution when used in conjunction with the aforementioned aqueous solution of anionic charge modifying agent, that adequate bonding of the charge modifying agent to the microporous membrane is obtained.

Both the anionic charge modifying agent and the cross-linking agent may be contacted with the membrane by dipping the membrane in the aqueous solutions of these compounds for a period of time sufficient to effect the desired degree of pick-up. Alternatively, the agents may be applied by spraying or contacting a wick or roll along the surface of the microporous membrane which almost immediately adsorbs and/or absorbs the aqueous solution due to the membrane's hydrophilicity.

Between each contacting step of the process for producing the membrane, the membrane is drained for a period of time sufficient to remove most of the water and chemical compound(s) not absorbed or adsorbed onto the surface of the membrane. The membrane may be transferred directly from the first contacting step to a subsequent contacting step, although this is less preferred. An intermediate treatment may also be a restrained drying step.

After the microporous membrane has been contacted with the aqueous solution(s), it may then be washed, dried and cured, preferably in a restrained condition to prevent shrinkage.

Preferably, prior to charge modifying the membrane film may be laminated to another membrane, or optionally laminated to a reinforcing web to form a reinforced laminated filtration membrane. Unique reinforced membranes and their methods of production are described and claimed in Assignee's U.S. Ser. No. 332,068 to Barnes et al filed Dec. 18, 1981, the entire disclosure of which is incorporated herein by reference. Preferably, lamination is accomplished by passing the plurality of layers juxtaposed upon each other through heated rollers to heat laminate and dry the membranes together. Preferably such drying is under restraint to prevent shrinkage. Drying of the membranes under restraint is described in the Assignee's Defensive Publication No. T-103,601, to Repetti published on Nov. 1, 1983. The entire disclosure of this publication is incorporated herein by reference. Generally, any suitable restraining technique may be used while drying, such as winding the membrane tightly about a dry surface, e.g. a drum. Bi-axial control is preferred and tensioning the laminated membrane is considered the most preferred.

The final drying and curing temperature for the filtration membrane should be sufficient to dry and cure the membranes. Preferably this temperature is from about 120° C. to 140° C. for minimization of drying time without embrittlement or other detrimental effects to the membranes. The total thickness of the filtration membrane is preferably from about 3 mils to about 30 mils and most preferably about 3 to 15 mils thick (dry thickness).

The filtration membrane may then be rolled and stored under ambient conditions for further processing into the usual commercial forms, for example, as discs or pleated cartridges by methods well known to the art.

Hollow fibers of membranes may be similarly and appropriately treated and processed into cartridges by methods known in the art.

The present invention provides an integral, coherent hydrophilic microporous membrane of retained internal pore geometry. The anionic charge modified membrane has an improved effective filtration rating relative to the untreated micro-reticulate polymer structure for cationic submicronic particulate contaminants and has a decreased adsorptive capacity for anionic submicronic particulate. These anionic particulates are often desirably retained in the liquid to be filtered, as for example, in cross-flow filtration a contaminant particulate that can cause pore blockage of the membrane. These properties are brought about by anionic charge sites or regions attached to, bonded to or populating the microstructure or pore surfaces throughout the membrane. These charge sites are effective over a broad range of pH's in enhancing filtration performance through eletrokinetic effects. The choice of anionic charge modifying agent, cross-linking agent and process conditions assures that the foregoing is accomplished without substantial pore size reduction or pore blockage.

The resulting membrane offers improved micrometer rating, for cationic submicronic particulate, at equivalent flow and capacity, with retention of membrane structure, yet without evidence of significant resin extractables, and improved cross-flow filtration effectiveness, particularly in plasmapheresis. In effect, the effective micrometer rating for cationic contaminant particles is less than the effective micrometer rating of the microreticulate membrane structure, but not for anionic particulate. Adsorption of critical or required anionic particulate or consistituents is minimized or eliminated. By the use of the term "effective micrometer rating for contaminant particles" it is meant the actual size of the particles that the membrane will quantitatively remove from the fluid being filtered. By the use of the term "effective micrometer rating of the microreticulate membrane structure" it is meant the size of the particulate that would pass through the membrane if all adsorptive effects of the membrane were eliminated.

For so-called sterile filtrations or plasmapheresis involving biological liquids, the filter is sanitized or sterilized by autoclaving or hot water flushing. Preparation for use in sterile filtration, requires that the membrane be sterilized as by treatment in an autoclave at 121° C. under 15 psig. for 1 hour. Accordingly, the anionic charge modified membrane must be resistant to this type treatment, and must retain its integrity in use. Any modification to the filter structure, especially brought about by chemical agents which may be unstable under conditions of treatment and use, must be scrutinized with care to minimize the prospect of extractables contaminating the filtrate, interfering with analysed and potentially introducing harmful toxins to a patient. Specifically, any such filter must meet the test standards in the industry, e.g. ASTM D 3861-79 (incorporated herein by reference), and generally have less than 5 mg. of extractables in 250 ml solvent (water at 80° C.; 35% ethanol at room temperature) for a 293 mm diameter disc. The membrane and process of this invention insures low extraction levels.

The resulting charge modified membrane is characterized by retention of internal microstructure, thus offering essentially the same flow characteristics as the untreated membrane.

The charge modified member additionally is easy to handle and readily formed into convoluted structures, e.g. pleated configurations. By reason of its retained flow characteristics, it may be employed directly into existing installations without pumping modifications. These favorable properties are secured without sacrifice to other characteristics. The membrane may also be constructed to meet or exceed extractable requirements.

Biological liquids, as that term is employed in the specification and claims, is a liquid system which is derived from or amenable to use with living organisms. Such liquids are ordinarily handled and processed under sanitary or sterile conditions and therefore require sanitized or sterilized media for filtration. Included within such term as isotonic solutions for intermuscular (im) or intravenous (iv) administration, solutions designed for administration per os, as well as solutions for topical use, biological wastes or other biological fluids which may contain cationic impurities, e.g., asbestos, alkali metal hydroxides or other cationic contaminants which are desirably isolated or separated for examination or disposal by immobilization or fixation upon or entrapment within a filter media. This can be accomplished with a minimum of removal or adsorption of desirable anionic particulates.

Filter membranes in accordance with this invention may be employed alone or in combination with other filter media to treat pharmaceuticals such as antibodies, saline solutions, dextrose solutions, vaccines, blood plasma, serums, sterile water or eye washes; beverages, such as cordials, gin, vodka, beer, scotch, whisky, sweet and dry wines, champagne or brandy; cosmetics such as mouthwash, perfume, shampoo, hair tonic, face cream or shaving lotion; food products such as vinegar, vegetable oils; chemicals such as antiseptics, insecticides, photographic solutions, electroplating solutions, cleaning compounds, solvent purification and lubrication oils, and the like. The membranes of this invention, particularly in the form of hollow microporous tubes, are also suitable for plasmapheresis. The flat membranes and hollow membrane tubes of this invention may also be used for cross-flow filtration.

By the use of the term "cross-flow filtration" it is meant the separation of undissolved particulate and suspended solids from a fluid, e.g., liquid, blood, mixture by passing or circulating, parallel or tangential to the surface of the membrane the fluid mixture producing a circulating effluent of concentrated particles or solids continuing to flow tangential to the membrane. Such techniques are well known in the art, particularly for plasmapheresis. It is believed that the anionic charge of the membrane prevents the predominantly anionic particulate or suspended solids in the fluid from clogging or blocking the pores by preventing excessive adsorption thereof, thus enhancing the efficiency and effectiveness of filtration.

Having now generally described this invention, the same will become better understood by reference to certain specific examples, which are included herein for the purposes of illustration only and are not intended to be limiting of the invention.

EXAMPLES

The following are the measurement and test procedures utilized in all the Examples.

Thickness

The dry membrane thickness was measured with a 1 inch (1.27 cm) diameter platen dial thickness gauge. Gauge accuracy was +0.00005 inches (+0.05 mils).

Initial Bubble Point (IBP) and Foam-All-Over Point (FAOP) Tests

A 47 mm diameter disc of the membrane sample is placed in a special test holder which seals the edge of the disc. Above the membrane and directly in contact with its upper face, is a perforated stainless steel support screen which prevents the membrane from deforming or rupturing when air pressure is applied to its bottom face. Above the membrane and support screen, the holder provides an inch deep capacity into which distilled water is introduced. A regulated air pressure is increased until a first stream of air bubbles is emitted by the water wetted membrane into the quiescent pool of water. The air pressure at which this first stream of air bubbles is emitted is called the Initial Bubble Point (IBP) of the largest pore in that membrane sample--see ASTM F-316-70 which is incorporated herein by reference.

Once the Initial Bubble Point pressure has been determined and recorded, the air pressure is further increased until the air flow through the wetted membrane sample, as measured by a flow meter in the line between the regulator and the sample holder, reaches 1000 cc/min. The air pressure at this flow rate, is called the Foam-All-Over-Point (FAOP), and is directly proportional to the mean pore diameter of the sample membrane. In this series of tests, these two parameters (IBP and FAOP) are used to determine if any change has occurred in the maximum or mean pore size of the membrane sample as a result of the charge modifying process utilized.

Flow Rate Test

A 47 mm diameter disc of the membrane sample is placed in a test housing which allows pressurized water to flow through the membrane. Prefiltered water is passed through the membrane sample at a pressure differential of 5 psid. A graduated cylinder is used to measure the volume of water passed by the membrane sample in a one minute period. In this series of tests this parameter is used in conjunction with the IBP and FAOP to determine if any reduction in pore size or pore blockage has occurred as a result of the anionic charge modifying process utilized.

METHYLENE BLUE DYE TESTS FOR ANIONIC MEMBRANE

A 47 mm diameter disc of the membrane sample is placed in a test housing which allows pressurized water to flow thru the membrane. The challenge solution consists of distilled water at a pH of 7.0, and methylene blue dye. The dye inlet concentration is adjusted to produce a 34 percent transmittance at a wavelength of 660 nm, as measured on a Bausch & Lomb Spectronic 710 Spectrophotometer. By means of a peristaltic pump the challenge solution is flowed thru the membrane sample at a flow rate of 28 ml/min. The transmittance of the effluent is measured by passing it thru a constant flow cell in the aforementioned spectrophotometer. The effluent transmittance and pressure drop across the membrane is measured and recorded as a function of time. The test is terminated when the effluent transmittance increases to 45 percent of the inlet transmittance. In this series of tests, the length of time that it takes to reach the 45 percent transmittance in the effluent is called the "breakthru" time. Since methylene blue is a low molecular weight cationic dye incapable of being mechanically removed (filtered) by the membrane, this breakthru time is proportional to the anionic adsorptive capacity of the membrane sample. This time is therefore used to determine the effectiveness of the charge modification technique.

Extractables (ASTM D-3861-79)

Extractables are determined by ASTM D-3861-79. The quantity of water-soluble extractables present in membrane filters is determined by immersing a preweighed membrane in boiling reagent grade water for an extended time and then drying and reweighing the membrane. A control membrane is employed to eliminate weighing errors caused by balance changes or changing moisture content of the membrane in the weighing procedures. Weight changes of the control membrane are applied as a correction factor to the weight change of the test membrane filters.

EXAMPLE I Preparation of Microporous Membrane

A representative nylon 66 membrane of 0.22 micrometer nominal rating, having a nominal surface area of about 13 m² /g, an Initial Bubble Point of about 47 psi, a Foam-All-Over-Point of about 52 psi was prepared by the method of Marinaccio et al, U.S. Pat. No. 3,876,738, utilizing a dope composition of 16 percent by weight nylon 66 (Monsanto Vydyne 66B), 7.1% methanol and 76.9% formic acid, a quench bath composition of 25% methanol, 75% water by volume (regenerated as required by the method of Knight et al, U.S. Pat. No. 3,928,517) a casting speed of 24 inches/minute (61 cm/min.), and a quench bath temperature of 20° C. The membrane was cast just under the surface of the quench bath by application to a casting drum rotating in the bath (9 to 10 mils as cast wet, to obtain 4.5 to 5.5 mils dry) and allowed to separate from the drum about 90° of arc from the point of application. A portion of the uniform opaque film was dried (in restrained condition to resist shrinkage) in a forced air oven at 80°-90° C. for 30 minutes.

EXAMPLE II Preparation of Representative Cationic Charge Modified Membrane*

Two layers of wet microporous membrane, made as in Example I, were laminated together and dried to 20-25% moisture.

The double layer of membrane was introduced into a 1.25% by weight solution of Hercules R4308. The pH of the bath was 10.5.

This bath was produced by diluting 38lbs. (17.17 Kg.) of Hercules R4308 resin from its initial 20% by weight concentration to 5%. Five normal (5N) sodium hydroxide solution was then added to raise the pH to 10.5. The solution was then diluted with D.I. water having greater than 150,000 ohm-cm resistivity in a ratio (volume) 2.5:1. The total volume of bath solution was 60 gallons.

Upon exiting this bath, the membrane was wiped on the bottom surface to remove excess water. A 3 minute air soak with cool air movement was used before the membrane entered the secondary charge modifying agent bath.

This bath was produced by adding 0.023% tetraethylene pentamine by weight or 0.113 lbs. (0.0513 kg) to 60 gallons (227. liters) of D.I. water (at least 150,000 ohm -cm resistivity). The pH was about 9. The immersion conditions are identical to the first bath of primary charge modifying agent. The membrane was then wrapped around a take up roll. The take up roll of wet membrane was stored for at least 3 hours. The roll was then dried at 250° F. (121° C.) for 3 minutes to complete the reaction of the charge modifying agents.

The membrane was then washed in a subsequent operation and checked for extraction levels.

EXAMPLE III

In all of the following Examples nylon membrane was treated with a water solution of charge modifying agent and, where indicated, a cross-linking agent. Since solubility of some cross-linking agents in water is limited, the agent was first diluted in alcohol and then mixed with the aqueous solution of anionic charge modifying agent. The membrane was drained, washed and dried in an oven at from 100° C. to 125° C. for 15-20 minutes. The membrane was then washed. The treatments and test results are tabulated on the attached Table 1.

                                      TABLE 1                                      __________________________________________________________________________              2                                                                     A    1   Starting  3                                                           Sample                                                                              Test                                                                               Membrane  Treatment                                                   Number                                                                              No. Description                                                                              Mode       COMMENTS                                         __________________________________________________________________________     C6-28-1                                                                              1  0.2 micron, nylon                                                                        PSSA.sup.1 /EGDGE.sup.2                                                                   4% PSSA, 2.7% EGDGE in treatment solution.       C6-28-2                                                                              2  *0.2 micron, nylon                                                                       PAA.sup.3  1.3% PAA in treatment solution.                        3  charged cationically                                                                     PAA                                                         C6-31-1                                                                              4  *0.2 micron, nylon                                                                       PAA        1% PAA in treatment solution.                    C6-32-1                                                                              6  0.2 micron, nylon                                                                        PSSA/EGDGE 5.5% PSSA, 1.8% EGDGE in treatment                                             solution                                         C6-34-1                                                                              7  0.2 micron, nylon                                                                        PAA/PLURONIC.sup.4                                                                        Treatment with 1% Pluronic solution                                            followed by 1% PAA solution.                     C6-34-2                                                                              8  0.2 micron, nylon                                                                        1884.sup.5 /PAA                                                                           Treatment with 1% solution 1884 (cationic                                      agent) followed by 1%                                                          PAA solution.                                    C6-35-1                                                                              9  0.2 micron, nylon                                                                        1884/PMA.sup.6                                                                            Treatment with 1% solution 1884 (cationic                                      agent) followed by 1%                                                          PAA solution.                                    C6-35-2                                                                             10  0.2 micron, nylon                                                                        PAA/PLURONIC                                                                              .88% PAA, .12% Pluronic treatment                                              solution.                                        C6-35-4                                                                             11  0.2 micron, nylon                                                                        PAA/PLURONIC                                                                              1.76% PAP, .12 Pluronic treatment                __________________________________________________________________________                                   solution                                          *Cationic charge modified pursuant to "Best Mode" in USSN 314,307 to           Ostreicher et al.                                                        

    C6-36-1                                                                             12  0.2 micron, nylon                                                                        PAA/PLURONIC                                                                              1.58% PAA, .21% Pluronic treatment                                             solution                                         C6-36-2                                                                             13  0.2 micron, nylon                                                                        PAA/PLURONIC                                                                              3.53% PAA, .12% Pluronic treatment                                             solution                                         C6-37-1                                                                             14  0.2 micron, nylon                                                                        PAA/PLURONIC                                                                              3.5% PAA, .12% Pluronic treatment solution       C6-41-2                                                                             15  0.45 micron, nylon                                                                       4308.sup.7 -TEPA.sup.8 */PAA                                                              Cationic solution followed by 1.3% PAA           C6-44-2                                                                             16  0.65 micron, nylon                                                                       PAA/C-303.sup.9                                                                           1.3% C-303, 3.6% PAA solution                    C6-45-2                                                                             17  0.65 micron, nylon                                                                       4308-TEPA*/PAA                                                                            Cationic solution followed by 2.0% PAA           C6-46-1                                                                             18  0.65 micron, nylon                                                                       PAA/C-303  5% C-303, 13% PAA solution                       C6-46-2                                                                             19  0.65 micron, nylon                                                                       PSSA/C-35201.sup.10                                                                       4.3% C-35201, 5% PSSA solution                   C6-47-1                                                                             20  0.65 micron, nylon                                                                       PSSA/C-35201                                                                              1.44% C-35201, 1.6% PSSA treatment                                             solution                                         C6-47-2                                                                             21  0.2 micron, nylon                                                                        PSSA/C-35201                                                                              1.44% C-35201, 1.6% PSSA treatment                                             solution                                         C7-4-1                                                                              22  0.2 micron, nylon                                                                        PAA/C-303  3.6% PAA of mw 104,000 and 1.3% C-303                                          treatment solution.                              C7-4-2                                                                              23  0.45 micron, nylon                                                                       PAA/C-303  3.6% PAA of mw 104,000, 1.3% C-303                                             treatment solution.                              C7-9-2                                                                              24  0.45 micron, nylon                                                                       PAA/C-303  2.1% PAA of mw 104,000, .77% C-303                                             treatment solution.                              C7-14-2                                                                             25  0.20 micron, nylon                                                                       PAA/C-303  2.1% PAA of mw 104,000, .77% C-303                                             treatment solution.                              C7-16-1                                                                             26  0.45 micron, nylon                                                                       PAA/C-303  1% PAA of mw 104,000, .37% C-303 treatment                                     solution.                                        C7-17-1                                                                             27  0.45 micron, nylon                                                                       PAA/C-303  1.2% PAA of mw 243,000, .43% C-303                                             treatment solution.                              C7-18-1                                                                             28  0.45 micron, nylon                                                                       PAA/C-303  .5% PAA of mm 243,000, .19% C-303 treatment                                    solution.                                        C8-30-1                                                                             29  0.45 micron, nylon                                                                       PAA/B-65.sup.11                                                                           Hollow fibers 2.% PAA, 1.5% B-65 treatment                                     solution.                                        C9-48-2                                                                             30  0.45 micron, nylon                                                                       PAA/B-65   1.% PAA, .75%, B-65 treatment solution.          C10-1-1                                                                             31  0.45 micron, nylon                                                                       PAA B-65   1.% PAA, .75%, B-65 treatment solution.          C10-47-1                                                                            32  0.2 micron, nylon                                                                        DOWFAX.sup.12                                                                             1% DOWFAX treatment solution.                    C10-47-2                                                                            33  0.2 micron, nylon                                                                        PAA/B-65   1% PAA, .75% B-65 treatment                      __________________________________________________________________________                                   solution.                                         *Cationic charge modifying pursuant to USSN 314,307 to Ostreicher et al. 

                    2                                                              A    B       1  Starting  3        4             5                             Sample                                                                              Starting                                                                               Test                                                                              Membrane  Treatment                                                                               Before Treatment                                                                             After Treatment               Number                                                                              Membrane                                                                               No.                                                                               Description                                                                              Mode     IBP                                                                               FAOP                                                                               FLOW                                                                               MB IBP                                                                               FAOP                                                                               FLOW                                                                               MB                 __________________________________________________________________________     C6-28-1                                                                             170-B17-0102                                                                            1 0.2 micron, nylon                                                                        PSSA.sup.1 /EGDGE.sup.2                                                                 43 47  105 2.4                                                                               -- --  --  --                 C6-28-2                                                                             141-A36-02                                                                              2 *0.2 micron, nylon                                                                       PAA.sup.3                                                                               53 60  66  1.5                                                                               -- --  --  --                      141-A36-01                                                                              3 charged cationically                                                                     PAA      53 60  66  1.5                                                                               -- --  --  --                 C6-31-1                                                                             141-A36-02                                                                              4 *0.2 micron, nylon                                                                       PAA      53 60  66  1.5                                                                               -- --  --  --                      141-A36-01                                                                              5 charged cationically                                                                     PAA      53 60  66  1.5                                                                               47.5                                                                              61.5                                                                               70.0                                                                                73.0              C6-32-1                                                                             170-B17-0102                                                                            6 0.2 micron, nylon                                                                        PSSA/EGDGE                                                                              43 47  105 2.4                                                                               39.0                                                                              42.0                                                                               100.0                                                                               94.0              C6-34-1                                                                             170-B17-0120                                                                            7 0.2 micron, nylon                                                                        PAA/     43 47  105 2.4                                                                               34.0                                                                              37.0                                                                               88.0                                                                                43.0                                        PLURONIC.sup.4                                       C6-34-2                                                                             170-B17-0102                                                                            8 0.2 micron, nylon                                                                        1884.sup.5 /PAA                                                                         43 47  105 2.4                                                                               42.0                                                                              47.0                                                                               84.0                                                                                42.0              C6-35-1                                                                             170-B17-0102                                                                            9 0.2 micron, nylon                                                                        1884/PMA.sup.6                                                                          43 47  105 2.4                                                                               -- --  --  --                 C6-35-2                                                                             170-B17-0102                                                                           10 0.2 micron, nylon                                                                        PAA/     43 47  105 2.4                                                                               36.0                                                                              39.0                                                                               98.0                                                                                55.3                                        PLURONIC                                             C6-35-4                                                                             170-B17-0102                                                                           11 0.2 micron, nylon                                                                        PAA/     43 47  105 2.4                                                                               37.0                                                                              44.0                                                                               92.0                                                                               171.3                                        PLURONIC                                             C6-36-1                                                                             170-B17-0102                                                                           12 0.2 micron, nylon                                                                        PAA/     43 47  105 2.4                                                                               36.0                                                                              42.0                                                                               98.0                                                                               170.6                                        PLURONIC                                             C6-36-2                                                                             170-B17-0102                                                                           13 0.2 micron, nylon                                                                        PAA/     43 47  105 2.4                                                                               40.0                                                                              44.0                                                                               80.0                                                                               292.7                                        PLURONIC                                             C6-37-1                                                                             170-B17-0102                                                                           14 0.2 micron, nylon                                                                        PAA/     43 47  105 2.4                                                                               -- --  --  --                                           PLURONIC                                             C6-41-2                                                                             246-D12-0204                                                                           15 0.45 micron, nylon                                                                       4308.sup.7 -TEPA.sup.8 /                                                                34 38  151 -- 34.0                                                                              38.0                                                                               160.0                                                                              --                                           PAA                                                  C6-44-2                                                                             252-D25-09                                                                             16 0.65 micron, nylon                                                                       PAA/C-303.sup.9                                                                         21 23  400 -- 21.5                                                                              24.0                                                                               402.0                                                                              --                 C6-45-2                                                                             252-D25-09                                                                             17 0.65 micron, nylon                                                                       4308-TEPA/PAA                                                                           21 23  400 -- 21.0                                                                              23.5                                                                               420.0                                                                              --                 C6-46-1                                                                             252-D25-09                                                                             18 0.65 micron, nylon                                                                       PAA/C-303                                                                               21 23  400 -- 20.5                                                                              23.0                                                                               376.0                                                                              --                 C6-46-2                                                                             252-D25-09                                                                             19 0.65 micron, nylon                                                                       PSSA/C-35201.sup.10                                                                     21 23  400 -- -- --  --  --                 C6-47-1                                                                             252-D25-09                                                                             20 0.65 micron, nylon                                                                       PSSA/C-35201                                                                            21 23  400 -- 20.0                                                                              23.0                                                                               208.0                                                                              --                 C6-47-2                                                                             170-B17-0102                                                                           21 0.2 micron, nylon                                                                        PSSA/C-35201                                                                            43 47  105 2.4                                                                               -- --  --  --                 C7-4-1                                                                              270-E13-0102                                                                           22 0.2 micron, nylon                                                                        PAA/C-303                                                                               47 51  90  2.5                                                                               47.0                                                                              53.0                                                                               74.0                                                                               220.0              C7-4-2                                                                              289-E34-0304                                                                           23 0.45 micron, nylon                                                                       PAA/C-303                                                                               32 54  190 2.5                                                                               31.0                                                                              34.0                                                                               200.0                                                                              110.0              C7-9-2                                                                              289-E34-0304                                                                           24 0.45 micron, nylon                                                                       PAA/C-303                                                                               32 54  190 2.5                                                                               31.0                                                                              35.0                                                                               190.0                                                                              100.0              C7-14-2                                                                             290-E40-0304                                                                           25 0.20 micron, nylon                                                                       PAA/C-303                                                                               45.2                                                                              --  68  -- 52.0                                                                              56.0                                                                               76.0                                                                               157.0              C7-16-1                                                                             289-E34-0304                                                                           26 0.45 micron, nylon                                                                       PAA/C-303                                                                               32 54  190 2.5                                                                               32.0                                                                              35.0                                                                               200.0                                                                              145.0              C7-17-1                                                                             289-E34-0304                                                                           27 0.45 micron, nylon                                                                       PAA/C-303                                                                               32 54  190 2.5                                                                               32.0                                                                              35.0                                                                               192.0                                                                              207.0              C7-18-1                                                                             289-E34-0304                                                                           28 0.45 micron, nylon                                                                       PAA/C-303                                                                               32 54  190 2.5                                                                               29.0                                                                              33.0                                                                               164.0                                                                              100.0              C8-30-1-2                                                                           Hollow Fibers                                                                          29 0.45 micron, nylon                                                                       PAA/B-65.sup.11                                                                         30 34  --  -- -- --  --  --                 C9-48-2                                                                             S20881  30 0.45 micron, nylon                                                                       PAA/B-65 30.2                                                                              36  180 -- 33.0                                                                              37.0                                                                               168.0                                                                               72.0              C10-1-1                                                                             S20881  31 0.45 micron, nylon                                                                       PAA/B-65 30.2                                                                              36  180 -- -- --  --  --                 C10-47-1                                                                            S22462  32 0.2 micron, nylon                                                                        DOWFAX.sup.12                                                                           42.3                                                                              47.8                                                                               92.5                                                                               6.1                                                                               43.0                                                                              47.0                                                                               97.0                                                                                13.0              C10-47-2                                                                            S22462  33 0.2 micron, nylon                                                                        PAA/B-65 42.3                                                                              47.8                                                                               92.5                                                                               6.1                                                                               42.0                                                                              48.0                                                                               93.0                                                                               --                 __________________________________________________________________________      FOOTNOTES:-                                                                    IBP means Inital Bubble Point, psig.                                           FAOP means Foam All Over Point, psig.                                          FLOW aforedescribed "FLOW" test, ml./min.                                      MB means aforedescribed Methylene Blue Test, mins.                             *Cationically charge modified pursuant to "Best Mode" in USSN 314,307 to       Ostreicher et al.                                                              .sup.1 PSSA is polystyrene sulfonic acid                                       (POLYSCIENCE):                                                                 ##STR6##                                                                       .sup.2 EGDGE is ethylene glycol diglycidyl ether (POLYSCIENCE).                .sup.3 PAA is polyacrylic acid (GOODRITE K702, 722, 732, 752,                  GOODRICH):                                                                     ##STR7##                                                                       .sup.4 Pluronic is a polyol (BASF WYANDOTTE).                                  .sup.5 1884 is polyamide  polyamine epichlorohydrin resin (POLYCUP,            HERCULES).                                                                     .sup.6 PMA is polymaleic anhydride (GANTREZ AN,                                GAF):                                                                          ##STR8##                                                                       .sup.7 4308 is polyamido  polyamine epichlorohydrin resin (POLYCUP,            HERCULES).                                                                     .sup.8 TEPA is tetraethylene pentamine (UNION                                  H.sub.2 N(CH.sub.2).sub.2 NH(C--H.sub.2).sub.2 NH(CH.sub.2).sub.2              NH(CH.sub.2).sub.2 NH.sub.2-                                                   .sup.9 C-303 is hexa methoxymethyl melamine resin (CYMEL 303, AMERICAN         CYANAMID).                                                                     .sup.10 C35201 is water borne epoxy resin (CMD 35201, CELANESE).               .sup.11 B65 is methylated urea formaldehyde resin (BEETLE 65, AMERICAN         CYANAMID).                                                                     .sup.12 Dowfax is sodium mono and didodecyl disulfonated diphenyloxide         (DOW).                                                                   

EXAMPLE IV Evaluation of Membranes for Plasmapheresis

Four nylon membranes, 0.45 micron untreated (Example I), 0.45 micron anionic (Sample 24) or 0.45 micron cationic (Example II) and 0.2 micron untreated (Example I), were evaluated for the separation of plasma and cellular components of blood.

The test criteria is the rate of hemoglobin appearance into the plasma phase vs. the filtration rate. The test procedure and results are described below. The 0.2 micron untreated membrane gave the best results, however, the charged modified 0.45 micron membranes performed better than the untreated 0.45 micron membrane. Four membranes (0.45 micron untreated, 0.45 micron anionic, 0.45 micron cationic, and 0.2 micron untreated) were presented for comparison with the membrane employed most frequently in prior studies with this system, SARTORIUS 0.45 micron cellulose nitrate.

Methods and Apparatus

The system employed in these studies is shown in FIG. I. A modified SARTORIUS membrane cell is assembled with three 16×16 cm membrane sheets and connected as shown. Plasma (250 ml) is circulated over the membranes as a pretreatment. Approximately 300 ml of whole human blood (drawn no more than 3 hours prior to the run) is added to a beaker containing 500 IU of heparin. The blood pump is started and set to read "10" on the speed meter (about 38 ml/min). After about 4 minutes for stabilization and sufficient washout of the filtrate side of the cell by fresh filtrate, the filtration rate is measured by diverting the filtrate into a graduated cylinder and samples of filtrate and blood are taken for analysis. The blood pump speed meter reading is incremental by 5 and the procedure is repeated until two obviously pink/red samples have been obtained.

Filtrate samples are analyzed for hemoglobin (Hgb) by spectrophotometric techniques. Blood samples are analyzed for hematocrit, and plasma and total Hgb by a Coulter counter. One sample each of blood and filtrate is selected for protein electrophoresis.

Results and Discussion

Observed and computed results of the membrane tests are presented in Tables II through VI. Each table lists; the input blood flow rate, QI, the filtration rate, QF; the concentration of Hgb in the plasma phase of the inflowing blood, C_(I). the Hgb concentration in the filtrate, C_(F) ; and the rate of Hgb appearance into the plasma phase, D, for the indicated membrane where D is approximated as:

    D=Q.sub.I (C.sub.F -C.sub.I)/100.

All values are for a three membrane system.

The optimally functioning primary separation unit of a plasmapheresis system must be capable of producing the greatest flow of plasma with the least damage to the cellular blood components. In the terms employed above, Q_(F) must be maximized while holding D to some arbitrarily acceptable value. The evaluation of the five membranes tested can most readily be performed in this manner from a plot of the Hgb appearance rate, D, as a function of the filtrate rate, Q, shown in FIG. 2. The curve furthest to the lower right will specify the membrane of choice, based on the above stated criteria. Clearly, the 0.2μ untreated membrane gave the best results. At the Hgb appearance rate 1.5 mg/min, this test produced 9.3 ml/min of filtrate. The second best performer, the 0.45μ negative gave 74 percent (6.9 ml/min) of this value for the same criterion. The control membrane (Satorius 0.45μ cellulose nitrate) produced only 4.6 ml/min or 49 percent as much filtrate as did the 0.2μ.

Interestingly, the 0.45μ untreated membrane gave the poorest performance of all while the anionic and cationic modifications of this membrane produced filtration rates about midway between those of the neutral 0.2 and 0.45μ. This may be due to a greater number of cells being convected into the 0.45μ membrane with subsequent plugging of the membrane pore structures. Subjective visual examination of the membranes after each run found that "staining" of the membranes (probably due to the cells impacted into pores) appeared to correlate inversely with the maximum filtration rate, lending some credence to this hypothesis. This observation suggests that the process involved in modifying the membranes may make them less susceptible to plugging by such a mechanism, thus raising the maximum filtration rate. The anionic modification gave better results than the cationic.

All protein electrophoresis results for the filtrate samples had the appearance of normal plasma results.

                  TABLE II                                                         ______________________________________                                         Results of the Sartorius Cellulose Nitrate 0.45u Membrane Test                 Q.sub.I  Q.sub.F  C.sub.I    C.sub.F                                                                               D                                          (ml/min) (ml/min) (mg/dl)    (mg/dl)                                                                               (mg/min)                                   ______________________________________                                          60      3.0      24.6       24.6   *                                          100      4.7      28.6       30.1   1.50                                       132      5.3      35.1       36.9   2.38                                       163      7.0      41.0       42.4   2.28                                       192      7.3      53.6       56.1   4.80                                       223      6.5      77.9       82.0   9.14                                       ______________________________________                                          *Undetectable                                                            

                  TABLE III                                                        ______________________________________                                         Results of the 0.45u Untreated Membrane Test                                   Q.sub.I  Q.sub.F  C.sub.I    C.sub.F                                                                               D                                          (ml/min) (ml/min) (mg/dl)    (mg/dl)                                                                               (mg/min)                                   ______________________________________                                         37.8     1.1      18.4       18.5   0.04                                       68.6     1.3      18.7       18.8   0.07                                       99.4     2.1      19.2       19.3   0.10                                       130      3.5      24.1       25.2   1.43                                       161      4.4      40.6       43.6   4.83                                       192      5.4      68.2       72.4   8.06                                       ______________________________________                                    

                  TABLE IV                                                         ______________________________________                                         Results of the 0.2u Untreated Membrane Test                                    Q.sub.I  Q.sub.F  C.sub.I    C.sub.F                                                                               D                                          (ml/min) (ml/min) (mg/dl)    (mg/dl)                                                                               (mg/min)                                   ______________________________________                                         37.8     4.7      15.7       19.2   1.3                                        68.6     6.4      20.0       22.3   1.6                                        99.4     7.8      23.1       24.3   1.2                                        130      9.2      26.8       27.9   1.4                                        161      9.6      31.8       32.9   1.8                                        192      9.9      38.7       40.1   2.7                                        223      10.1     80.8       87.9   15.8                                       253      10.3     139.       148.   22.8                                       ______________________________________                                    

                  TABLE V                                                          ______________________________________                                         Results of the 0.45u Positive Membrane Test                                    Q.sub.I  Q.sub.F  C.sub.I    C.sub.F                                                                               D                                          (ml/min) (ml/min) (mg/dl)    (mg/dl)                                                                               (mg/min)                                   ______________________________________                                         37.8     2.9      26.1       27.9   0.7                                        68.6     4.8      29.7       31.6   1.3                                        99.4     6.1      34.2       35.9   1.7                                        130.     73       47.8       51.7   5.1                                        161.     8.3      137.       158.   33.8                                       ______________________________________                                    

                  TABLE VI                                                         ______________________________________                                         Results of the 0.45u Negative Membrane Test                                    Q.sub.I  Q.sub.F  C.sub.I    C.sub.F                                                                               D                                          (ml/min) (ml/min) (mg/dl)    (mg/dl)                                                                               (mg/min)                                   ______________________________________                                         37.8     4.0      26.9       27.6   0.26                                       68.6     5.6      29.1       30.1   0.69                                       99.4     7.0      34.8       36.5   1.69                                       130.     6.9      48.1       51.2   4.03                                       161.     7.2      64.9       68.1   5.15                                       192.     7.3      114.       122.   15.36                                      ______________________________________                                    

EXAMPLE V Evaluation of Hollow Fiber Modules for Blood Component Separation

The present evaluation involves six hollow fiber modules: two each of the unmodified fiber, anionic (negative) surface modified, and cationic (positive) surface modified.

The anionic fibers were prepared pursuant to Sample 29 (C-8-30-2). The cationic fibers were treated in a manner similar to Example II (C-8-31-1)

Apparatus and Methods

The system employed in these studies is shown in FIG. 3. It consists of a Travenol Laboratories roller-type blood pump (used on the Travenol RSP hemodialyzer), clot filter, 0-760 mm Hg pressure gauge, Swagelok fittings for connection to the hollow fiber module, Manostat Calcuflow flow meter, and fluid reservoir with stirrer.

The apparatus is assembled with the desired test module oriented vertically (with flow from top to bottom) and 250 ml of human plasma is added to the reservoir beaker. The plasma is circulated through the system for 15 minutes at approximately 100 ml/min. This allows for leak checks and for deposition of plasma proteins on rough or otherwise biologically reactive surfaces. Pretreatment of the system in this manner has been shown to decrease the degree of hemolysis that occurs on the initial contact of the blood with the membrane. At the end of the pretreatment, the pump is stopped and the pump inlet line is transferred to a second reservoir beaker containing 250-300 ml of fresh human blood and 500 IU of heparin. An initial blood sample is taken from the beaker. The pump is restarted and the module and filtrate outlet lines are moved to the blood beaker when the first evidence of blood leaving the module is noted. Timing of the run begins at this point.

The remainder of the test is divided into intervals of ten minutes each. At the midpoint of each interval, the inlet pressure and filtration rate are recorded. At the end of each interval, a filtrate sample is taken for analysis. Each sample is immediately centrifuged and the plasma is separated from any cells or fragments that are present. This will lessen the likelihood of falsely high plasma hemoglobin values. The pump is incremented and the next interval begins. At the end of the test, a blood sample is taken from the beaker to provide a check on the mass balance.

Results and Discussion

Table VII lists the characteristics of the hollow fiber modules tested. Observed and computed results of the tests are presented in Tables VIII-XIII. Each table lists each input blood flow rate tested, Q_(I) (ml/min); the corresponding filtration rate, QF (ml/min); concentration of Hgb in the plasma phase of the inflowing blood at the end of the measurement interval, C_(I) (mg/dl); Hgb concentration in the filtrate at the end of the interval, C_(F) (mg/dl); and rate of Hgb release in the plasma, D (mg/min), where D is approximated as D=Q_(I) (C_(F) -C_(I))/100. The values for the Hgb appearance rate D have been corrected for the hemolysis effects of the blood pump and other hardware and represent only the effects produced by the test module.

It should be noted that blood leaks into the filtrate were a significant problem with three of the surface modified fiber modules: 8207-2 (anionic), 8207-5 (cationic) and 8207-6(cationic). In the test of module 8207-2 (anionic) the leak was so severe that it was difficult to distinguish between the fluid in the filtrate and blood outlet lines until the samples had been centrifuged. Normally, the filtrate has the appearance of plasma with slight brown or pink coloration. The extent to which this leakage affected the results is unknown.

FIG. 4 presents the filtration rate for each module as a function of the blood inflow rate. With the exception of the anionic unit 8207-2 (which developed the leak early in the test), the surface modified fibers produced greater filtration rates for a given blood flow rate than did the unmodified fibers. At an inflow rate of 300 ml/min, the modified fiber modules averaged about 29 percent more filtrate than the untreated fiber modules.

FIGS. 5-7 present the rate of hemoglobin appearance, D, as a function of the filtration rate Q_(F), for the various modules. FIG. 5 shows the performance of the unmodified fibers. Both modules exhibited relatively high initial hemolysis rates which declined sharply as the filtration rate increased. After reaching a minimum rate of hemolysis, corresponding to filtration rates of 40-45 ml/min, hemolysis increased with further increases in filtration rate. The minimum hemolysis rates for both modules were below the arbitrary standard of 1.5 mg/min. (By this standard, a patient with a plasma volume of 3 liters could be treated for 6 hours and have the plasma Hgb increase by 15 mg/dl. The normal plasma Hgb is about 7 ml/dl.)

FIG. 6 presents the results for the modules with the cationic modified fibers. Module 8207-5 performed similarly to the unmodified units, although the minimum hemolysis rate was not as low. The other module, 8207-6, exhibited extremely high initial hemolysis. The rate for this module did drop significantly and might have reached an acceptably low value if the blood leak had not occurred.

The results of the anionic surface modified fibers are presented in FIG. 7. Both modules performed similarly at low filtration rates with results much like the unmodified fibers. Interestingly, module 8207-7, which did not leak, did not exhibit the minimum in the hemolysis rate seen in other tests, but instead seemed to have an asymptote for the rate. This module's performance was far superior to all others. Module 8207-2 developed the blood leak before sufficient data could be collected to confirm this result. It should thus be possible to obtain high flow rates of low Hgb plasma with anionic surface modified fiber.

A problem common to all of the tests was significant initial hemolysis rates. There are a number of factors which may be responsible including roughness of the fiber walls, particularly at the entrance of the fiber. Microscopic examination of an unused module may be helpful in this determination and revision of the fiber potting procedure to produce smoother fiber ends may be advantageous for those modules to be used in blood separation.

Finally, a number of paired filtrate and outlet blood samples were tested to determine if sieving of albumin by the fibers could be detected. No significant difference was found in the results. If sieving occurs, it is probably quite small.

                  TABLE VII                                                        ______________________________________                                          Hollow Fiber Module Characteristics                                           ______________________________________                                         Module Codes   8148-48/49                                                                               8207-2/7  8207-5/6                                    Surface Modification                                                                          None      Anionic   Cationic                                                             (negative)                                                                               (positive)                                  Treatment Mode --        Sample 29 Example II                                  Number of fibers                                                                              130       120       120                                         Fiber ID (cm)  0.0376    .0378     0.0358                                      Fiber OD (cm)  0.0627    0.0638    0.0630                                      Fiber length (cm)                                                                             16        16        16                                          Internal Area (sq cm)                                                                         246       228       216                                         IBP (psi)      31.0      33.8      32.1                                        FAOP (psi)     34.2      37.0      36.0                                        FLOW (ml/min-psi-cm.sup.2)                                                                    0.37      0.38      0.35                                        Module Test Pressure (psi)                                                                    10        10        7/10                                        ______________________________________                                    

                  TABLE VIII                                                       ______________________________________                                         Module 8148-48 (Untreated) Data                                                Q.sub.I                                                                               Q.sub.F  P.sub.inlet                                                                            C.sub.I C.sub.F                                                                               D                                       (ml/min)                                                                              (ml/min) mmHg    (mg/dl) (mg/dl)                                                                               (mg/min)                                ______________________________________                                         116    21.8     *       55.2    65.6   12.1                                    174    29.0     *       73.9    76.7   4.9                                     249    33.3     *       82.6    83.5   2.2                                     322    39.1     *       90.0    90.6   1.9                                     396    45.0     *       119.2   120.9  6.7                                     ______________________________________                                          *Pressure monitor failed                                                 

                  TABLE IX                                                         ______________________________________                                         Module 8148-49 (Untreated) Data                                                Q.sub.I                                                                               Q.sub.F  P.sub.inlet                                                                             C.sub.I                                                                               C.sub.F                                                                               D                                       (ml/min)                                                                              (ml/min) mmHg     (mg/dl)                                                                               (mg/dl)                                                                               (mg/min)                                ______________________________________                                         116    23.5     225-238  47.1   53.9   7.9                                     174    30.0     353-373  65.0   67.5   4.4                                     249    36.0     472-503  81.9   83.5   4.0                                     322    42.5     607-647  92.6   93.3   2.3                                     396    55.2     749-790  126.0  127.8  7.1                                     ______________________________________                                    

                  TABLE X                                                          ______________________________________                                         Module 8207-5 (Cationic) Data                                                  Q.sub.I                                                                               Q.sub.F  P.sub.inlet                                                                             C.sub.I                                                                               C.sub.F                                                                               D                                       (ml/min)                                                                              (ml/min) mmHg     (mg/dl)                                                                               (mg/dl)                                                                               (mg/min)                                ______________________________________                                         116    20.5     266-273  35.0   40.7   6.6                                     174    27.0     389-407  48.2   50.2   3.5                                     249    36.5     531-553  61.7   63.1   3.5                                     322    45.0     672-703  77.1   78.2   3.5                                     ______________________________________                                    

                  TABLE XI                                                         ______________________________________                                         Module 8207-6 (Cationic) Data                                                  Q.sub.I                                                                               Q.sub.F  P.sub.inlet                                                                             C.sub.I                                                                               C.sub.F                                                                               D                                       (ml/min)                                                                              (ml/min) mmHg     (mg/dl)                                                                               (mg/dl)                                                                               (mg/min)                                ______________________________________                                         116    24.5     320-333  102.8  122.4  22.7                                    174    32.0     476-500  161.1  169.4  14.4                                    249    39.0     647-693  198.2  201.7  8.7                                     322    56.0     750      223.8  225.6  5.8                                     ______________________________________                                    

                  TABLE XII                                                        ______________________________________                                         Module 8207-2 (Anionic) Data                                                   Q.sub.I                                                                               Q.sub.F  P.sub.inlet                                                                             C.sub.I                                                                               C.sub.F                                                                               D                                       (ml/min)                                                                              (ml/min) mmHg     (mg/dl)                                                                               (mg/dl)                                                                               (mg/min)                                ______________________________________                                         116    17.5     258-272  49.6   57.9   9.6                                     174    24.2     423-445  75.9   80.1   7.3                                     249    31.0     580-615  90.5   92.1   4.0                                     322    38.5     750      118.8  123.2  14.2                                    ______________________________________                                    

                  TABLE XIII                                                       ______________________________________                                         Module 8207-7 (Anionic) Data                                                   Q.sub.I                                                                               Q.sub.F  P.sub.inlet                                                                             C.sub.I                                                                               C.sub.F                                                                               D                                       (ml/min)                                                                              (ml/min) mmHg     (mg/dl)                                                                               (mg/dl)                                                                               (mg/min)                                ______________________________________                                         116    23.0     272-283  33.1   37.9   5.6                                     174    32.0     408-426  48.8   51.1   4.0                                     249    38.0     572-605  60.2   61.3   2.7                                     322    49.0     735-780  76.7   77.9   3.9                                     396    70.4     780      89.5   90.2   2.8                                     ______________________________________                                    

EXAMPLE VI (8109, 8026, I.S. 16250)

Polysulfone was solubilized in 1,2-dichloroethane (DCE) and reacted with chlorosulfonic acid, washed throughly in DCE and redissolved in dimethylformamide (DFM). (It is important to note that the sulfonated polysulfone is not soluble in DCE as was the base polymer). At this point the sulfonated polymer is relatively free of chlorosulfonic acid and therefore could easily be handled in aqueous media.

Nylon microporous membranes have been charge modified with dilute solutions of the sulfonated polysulfone polymer (SPS). Such treatment should produce a membrane that is compatible with blood since red blood cells are negatively charged.

Untreated nylon microporous membrane (217-E13-0102) made pursuant to Example I, was charge modified using the sulfonated polysulfone polymer solution produced above. The polymer solution was further diluted to 1:2, 1:5, and 1:8 in dimethyl formamide (DMF). Microporous nylon membranes were equilibrated in the diluted polymer solutions, air dried and then challenged with a dilute solution (0.02 ppm) of methylene blue. Methylene blue is a cationic dye, i.e., a dye with an immobilized positive charge.

The treated membranes exhibited a negative charge when challenged with the methylene blue dye solution, as shown in Table XIV below.

                  TABLE XIV                                                        ______________________________________                                                                Flow                                                    *Conc. IBP    FAOP     Rate   Init  Final                                                                               Ret Time                              SPS    psi    psi      ml/min psi   psi  Min                                   ______________________________________                                         0      46     52       117    3.7   --    2                                    1:2    44     51        51    5.7   23.6 40                                    1:5    43     53       120    5.8   11.0 25                                    1:8    43     52       106    4.4    9.1 20                                    ______________________________________                                          *Relative concentrations of sulfonated polysulfone from batch sulfonated       polymer solution.                                                        

In effect, the nylon membrane has been coated with a polymer containing an immobilized negative charge, i.e., SO₃ ⁻. The methylene blue, as mentioned before, possesses a positive charge, i.e., CH₃ ⁺. The methylene blue is adsorbed to the SPS coated nylon membrane through the SO₃ ⁻ group on the sulfonated polysulfone. 

What is claimed is:
 1. A process for filtration of liquid having cationic particulate contaminants therein, comprising passing the liquid through a skinless hydrophilic anionic charge modified microporous filter membrane comprising:a skinless hydrophilic organic polymeric microporous filter membrane having an internal microstructure throughout said membrane, and a charge modifying amount of an anionic charge modifying agent bonded to substantially all of the membrane microstructure without substantial pore size reduction or pore blockage, wherein the charge modifying agent is a water soluble polymer having substituents thereon capable of bonding to the membrane and anionic functional groups, wherein the anionic functional groups are selected from the group consisting of carboxyl, phosphonous, phosphonic, sulfonic groups or mixtures thereof and modify the zeta potential of the membrane, whereby the cationic particulate contaminants are captured by the anionic charge modified microporous membrane and substantially removed from the liquid.
 2. The process of claim 1, wherein the organic polymeric microporous membrane is polyvinylidene fluoride.
 3. The process of claim 1, wherein the organic polymeric microporous membrane is esters of cellulose.
 4. The process of claim 1, wherein the organic polymeric microporous membrane is nylon.
 5. The process of claim 4, wherein the organic polymeric microporous membrane is previously cationically charge modified.
 6. The process of claim 4, wherein the organic polymeric microporous membrane is polyhexamethylene adipamide.
 7. The process of claim 1, wherein the charge modified membrane is sanitized or sterilized.
 8. The process of claim 1, wherein the anionic functional groups are carboxyl.
 9. The process of claim 1, wherein the anionic functional groups are sulfonic.
 10. The process of claim 1, wherein the anionic charge modifying agent is a water soluble organic polymer having a molecular weight of about 2,000 to 500,000.
 11. The process of claim 1, wherein the anionic charge modifying agent is poly(styrene sulfonic) acid having a molecular weight between 2,000 and 300,000.
 12. The process of claim 1, wherein the anionic charge modifying agent is poly(acrylic) acid having a molecular weight between 2,000 and 300,000.
 13. The process of claim 1, wherein the anionic charge modifying agent is bound to the membrane through a cross-linking agent.
 14. The process of claim 13, wherein the cross-linking agent is an aliphatic polyepoxide having a molecular weight of less than about 500, melamine formaldehyde or methylated urea formaldehyde.
 15. The process of claim 14, wherein the cross-linking agent is an aliphatic polyepoxide having a molecular weight of less than 500, and the polyepoxide is a di- or tri-epoxide.
 16. The process of claim 14, wherein the cross-linking agent is an aliphatic polyepoxide having a molecular weight of from about 146 to about
 300. 17. The process of claim 14, wherein the cross-linking agent is an aliphatic polyepoxide having a molecular weight of less than about 500, and the polyepoxide has the formula: ##STR9## wherein R is an alkyl of 1 to 6 carbon atoms and n is an integer from 2 to
 5. 18. The process of claim 14, wherein the cross-linking agent is the polyepoxide 1,4-butanediol diglycidyl ether of the formula: ##STR10## 